4D Multilayer
A reliable choice for complex restorations
Density ≥6.0 (g/cm³)
Flexural strength ≥800(MPa)
Chemical solubility <100 (μg·cm⁻²)
3D Plus Multilayer
More suitable for lifelike anterior restorations
Density ≥6.0 (g/cm³)
Flexural strength ≥600(MPa)
Chemical solubility <100 (μg·cm⁻²)
ST Multilayer
More suitable for durable posterior restorations
Density ≥6.0 (g/cm³)
Flexural strength ≥800(MPa)
Chemical solubility <100 (μg·cm⁻²)
SHT Multilayer
Solution for comprehensive restorations
Density ≥6.0 (g/cm³)
Flexural strength ≥800(MPa)
Chemical solubility <100 (μg·cm⁻²)
UT Multilayer
An excellent choice for anterior restorations
Density ≥6.0 (g/cm³)
Flexural strength ≥600(MPa)
Chemical solubility <100 (μg·cm⁻²)
ST White
Applicable to a wide range of restorations.
Density ≥6.0 (g/cm³)
Flexural strength ≥800(MPa)
Chemical solubility <100 (μg·cm⁻²)
ST-Ⅱ White
Applicable to a wide range of restoration materials.
Density ≥6.0 (g/cm³)
Flexural strength ≥800(MPa)
Chemical solubility <100 (μg·cm⁻²)
HT White
Better suitable for inlay restorations
Density ≥6.0 (g/cm³)
Flexural strength ≥800(MPa)
Chemical solubility <100 (μg·cm⁻²)
UT White
More suitable for veneers
Density ≥6.0 (g/cm³)
Flexural strength ≥600(MPa)
Chemical solubility <100 (μg·cm⁻²)
ST Color
Used for pre-stained quick restorations
Density ≥6.0 (g/cm³)
Flexural strength ≥800(MPa)
Chemical solubility <100 (μg·cm⁻²)
SHT Color
Pre-shaded time-saving restoration material.
Density ≥6.0 (g/cm³)
Flexural strength ≥800(MPa)
Chemical solubility <100 (μg·cm⁻²)